Abstract
Influence of the silicon content on the maximum magnetic flux density was studied on the sintered Fe-18Cr-2Mo alloy at applied magnetic field in three Oersted. The highest maximum magnetic flux densities in DC and AC magnetic field were attained at the content of two-percent silicon. The lower magnetic properties was observed for the three-percent silicon or more. The sintered density and the DC maximum magnetic flux density consequently were improved with the rise of sintering temperature. On the other hand the AC maximum magnetic flux density indicated the change of a decrease after an increase. An excess sintering temperature rather causes a lowering of AC maximum magnetic flux density. An increase of the resistivity contributes to an improvement of AC maximum magnetic flux density on the whole, but for the lower sintered density, tends to cause the deteriorating of AC maximum magnetic flux density. The comparison of measured and calculated value for the frequency dependence
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.