Abstract
Using three different kinds of mixed powder compacts; each composed of Ti+TiAl3+(Al-50V), Ti+ A1+(Al-50V) and Ti+TiAl3+V, the sintering behavior of Ti-6A1-4V ternary system was investigated mainly through dilatometric method and EPMA, in relation to an α2 phase.The results obtained are summarized as follows:(1) The α2 phase was observed to have widely developed in all of the above mentioned three specimens; at 1373 K during heating process.(2) This α2 phase has disappeared by the diffusional process in both Ti + TiAl3 + (Al-50V) and Ti + Al + (Al-50V) specimens after sintering at 1373 K for 3.6 ks, however in the Ti +TiAl3+V specimen, small amount of remaining α2 phase was observed.(3) The sintering conditions necessary to obtain homogenized structure were confirmed to be 1373 K×3.6 ks, 1473 K×3.6 ks and 1573 K×3.6 ks in the following order: Ti+TiAl3+(Al-50V), Ti+AI+(Al-50V) and Ti+TiAl3+V specimens.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Japan Society of Powder and Powder Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.