Mixture of aluminum, copper and titanium powders was mechanically alloyed and then the powder was heat-treated at various temperature. A change of structure of the powder with milling period was investigated by using XRD, DTA, SEM and EPMA. In the early stage of mechanical alloying, particles of Cu and Ti are deformed and dispersed in Al matrix, but degree of deformation of Ti particle is smaller than that of Cu particle.Particles of Cu and Ti become finer with the increasing of milling period, and they disperse homogeneously as the milling period reaches to 72.0ks. Intermetallic Al2Cu phase was observed in the powder mechanically alloyed for 21.6ks. In the powder heattreated at 773K intermetallic Al3Ti and AlCu phases were observed. The forming temperature of Al3Ti and AlCu phase decrease with the increasing of milling period.Intermetallic AlTi phase was observed at low temperature in the powder mechanically alloyed for 72.0ks.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Japan Society of Powder and Powder Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.