Abstract
Solution polymerization behaviors of L-lactide using single and mixed aluminium catalyst systems were studied. Triisobutylaluminium (TIBA) was a reference catalyst for mixing. For the /TIBA catalytic systems, the molecular weight of the resulting polylactide (PLA) decreased as the composition of increased. The higher molecular weight shoulder was revealed in their GPC curve. At TIBA of 80 mol% a bimodal GPC curve was shown. The conversion in the trimethylaluminium (TMA)/TIBA catalysts system decreased as the composition of TMA in the mixed catalyst increased. The conversion in the trioctylaluminium (TOA)/TIBA catalysts system decreased as the composition of TOA in the mixed catalyst increased. The unimodal molecular weight distribution was observed with the TOA/TIBA catalyst systems. The Al compounds-mixed catalyst could produce a higher molecular weight shoulder in the GPC curve.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.