AbstractThe structure of a hafnium crystal undergoing β → α (bcc → hcp) polymorphic transformation upon gradual cooling and the structure of Hf_55Ti_45 and Hf_30Ti_70 alloys formed under various kinetic conditions of polymorphic transformation are studied. The structure of the α phase in cast hafnium is shown to consist of lath crystals grouped into packets. The misorientations between separate laths in a packet are less than 1°. The Hf–Ti alloys in the cast state exhibit a mixed structure consisting of α-phase crystals of several morphological types. A structure of packet martensite is observed in the Hf–Ti alloys after quenching. Each packet includes laths of several crystallographic orientations. There is no regular alternation of differently orientated laths in the packet. The same set of α-phase orientations within an initial β-phase grain is observed independently of the cooling rate of the Hf–Ti alloys upon β → α polymorphic transformation. The misorientation of substructural elements within an α-phase crystal in the Hf–Ti alloys is ~5° for the cast state and ~2.2° after quenching.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.