Abstract
Nano-size Y2O3 : Eu3+ powders were prepared via the thermal decomposition of yttrium carbonate coprecipitate precursors doped with europium. The carbonate precursor, which was synthesized with aging and milling, was fired at 800 °C in air. Consequently, the powder with average diameter of 36 nm was obtained. The relative fluorescence intensity due to the 5D0→7F2 transition of Eu3+ in Y2O3 sample with average diameter of 36 nm shows about 40% compared with that of commercial Y2O3 : Eu3+ phosphor with average particle diameter of 3.7 μm. The effect of ball-milling treatment during the aging of carbonate coprecipitated precursor on the preparation of nano-size Y2O3 : Eu3+ powders was discussed. Also, the effect of average diameter on the fluorescence intensity in nano-size Y2O3 : Eu3+ phosphor was discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.