Abstract
The niobium capacitor showed somewhat more unstable characteristics than the commercial tantalum capacitors, but is nonetheless considered applicable as a future substitute for tantalum capacitors. In this study, niobium powder was fabricated by metallothermic reduction process using as the raw materials, KCl and KF as the diluents and Na as the reducing agent. The niobium particle size greatly decreased from 0.7um to 0.2 um as the amount of diluent increased. However if a higher surface area of powder is required, more diluents need to be used in the said method in order to produce niobium powder. The niobium powder morphology and particle size are very sensitive to a amount of sodium excess. The particle size of niobium powder increased with a increasing amount of sodium excess. When more diluent and sodium are used, the niobium powder will be contaminated with more impurities such as Fe, Cr, Ni so on.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Korean institute of surface engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.