Abstract
The effect of temperature on the ultimate tensile strength (σuts) and fracture elongation (δ) under tension of titanium nickelide (50.2 at.% Ni) with initial coarse-grained structure and structures after abc-pressing at 873K (alloy 1, true deformation е = 2.2) and after “step-by-step” pressing at 873K→673K (alloy 2, е = 4.2) are studied. The grain dimensions in the samples of alloy 1 (2-40 μm) are smaller than ones in initial samples (20-70 μm). The structure of alloy 2 is submicrocrystalline (grain/subgrain dimensions are 100-700 nm). It was found that the martensitic transformations (MT) B2←→B19ʹ had been observed under cooling and heating of initial samples. The sequences of В2→R→В19ʹ→В2 MT were observed in alloys 1 and 2 (R – the rhombohedral martensitic phase). The finish of B19ʹ→B2 MT take place in the temperature range 340-355 K. The tension tests were carried out at temperatures 293K, 343K and 473K (or 523 K), i.e. in the B19ʹ phase, pretransition temperature range and B2 phase, accordingly. The “stress-strain” dependences obtained at these temperatures are quantitavely the same for all samples. The martensitic plateau connected with the reorientation and/or generation of the B19ʹ martensitic crystallites are observed under tension of samples at 293K and 343K. No the generation of stress-induced B19ʹ martensite was observed under tension at 473K (or 523K). The increase of σuts was found after abc-pressing. The maximum values of σuts are observed under tension of samples of alloys 1 and 2 at 293K and 343K (in B19ʹ phase). The alloy 1 demonstrates the highest plasticity (δ about 80%) at temperature range 293-343 K. The σuts and δ decrease essentially (about 2 times) with the temperature increase to 473K (or 523K).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.