Abstract
(Sr⋅Ba)-La-Co M-type ferrite fine particles were prepared by the chemical coprecipitation and subsequent heat-treatment method. The chemical reagents used for the experiment were FeCl3⋅6H2O, BaCl2⋅6H2O, SrCl2.6H2O, LaCl3⋅7H2O, and CoCl2.6H2O. The chemical coprecipitation process was applied to the samples having the formula. {(SrO)1-x⋅(BaO)x⋅n/2(Fe2O3)}100-Y-Z(La2O3)Y(CoO)Z (n=6.0-12.0, x=0.0-1.0, y=1.0-10.0, z=1.0-10.0). The solution containing Sr2+, Ba2+, Fe3+, La3+, and Cot2+ was poured into solution of NaOH (pH=13.0). The precipitated products were boiled for 2h and they were carefully washed with water and dried. The obtained fine particles were heated at 950 to 1100°C for 2h in air to obtain the single phase of (Sr⋅Ba)-La-Co M-type ferrite fine particles. The best magnetic properties were observed for the sample with the composition of {(SrO)0.8⋅(BaO)0.2⋅3.5(Fe2O3)} 88.0 (La2O3)6.0(CoO)6.0, and magnetic properties were as follows: σs= 84.8 × 10-6 Wb⋅m/kg (67.5 emu/g), σr=42.8 × 10-6 Wb⋅m/kg (34.1 emu/g), HcJ=476.6 kA/m (5.98 kOe) and Tc=452.6°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Japan Society of Powder and Powder Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.