군용 도포직물의 내후성시험 대체에 대한 연구

Abstract

Purpose We would like to find the alternative method for the weathering test on rubber coated fabrics and adhesive-coated fabrics for the military products, KS M 0706 (Sunshine carbon arc) to KS M ISO 4892-2 (Xenon arc). Methods We measured the tensile strength of adhesive-coated fabrics and adhesive products treated with sunshine carbon arc and xenon arc during 100, 150 and 200 hours, respectively. All of the results were treated with statistical test, ANOVA method. We also validate the surface modifications caused by treatment method and time by using FT-IR ATR and, SEM. Results In case of the thick adhesive-coated fabrics (app. 1 mm), there was no distinctive difference on tensile strength by treatment method and time. In case of the thin mask hood (app. 0.22 mm) and TENT (app. 0.5 mm), there was distinctive difference on tensile strength. Especially, carbon arc showed a huge lowering properties. We could validate the curing from light and moisture, and the functional group change from cross-linking and oxidation using FT-IR ATR. In case of IBS, there was a surface cracks on SEM images. In case of mask hood, there was no distinctive differences, except for a particle falling from decreased affinity between rubber and particles caused by carbon arc. Conclusion We concluded that there was no problems for changing xenon arc weathering test with same treatment time on IBS, KM7, K21 and adhesive products. In case of TENT and mask hood, there was a difference in tensile strength in accordance with the change of the treated time and method. Key words: Weathering Test, Coated Fiber, Carbon Arc, Xenon Arc