Abstract
Shot-peening effects on the fatigue behavior of bearing steel were investigated under the high cyclic loading. Hourglass shape specimens were made of bearing steel(JIS-SUJ2) for rotary bending fatigue tests. Two kinds of treatments were performed : a heat treatment and a shot-peened surface treatment after the heat treatment. The fracture surfaces of specimens were classified into two types of fracture mode : the surface fracture mode induced by a surface defect and the internal fracture mode induced by a nonmetallic inclusion. Inclusion depth and shape affected considerably the fatigue life. Shot-peening treatment improved much the fatigue life of the bearing steel under low and high levels of cyclic loads. Probabilistic-stress-life (P-S-N) curves were suggested for the reliable fatigue life estimation of the improved bearing steel.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Transactions of the Korean Society of Mechanical Engineers A
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.