Abstract
Zirconia graphite refractory is used in continuous casting of steel. Slag corrosion resistance influence on time of casting. With factorial experiment 25-1 influence mixture of refractory (content of graphite, silicon carbide, boron carbide) on oxidation resistance and interaction with mould powder (C/S = 1, F = 8 %) at 1400 °C. Boron carbide is better antioxidant than silicon carbide. Boron carbide 3 % mass decrease slag corrosion resistance of ZG-refractory. The thicknesses de-carbonized layer are within 1–7 mm Additives of boron carbide and silicon carbide reduce the thickness of the oxidized layer. It was established experimentally that the boron carbide has the best antioxidant properties than silicon carbide therefore, in the study circolatorio materials action SiC less effective than B4C.
Highlights
Шлаковый пояс погружного стакана во время эксплуатации подвергается следующим воздействиям: окисление кислородом воздуха углеродистой составляющей, растворение оксидной составляющей в шлаке, растворение углеродистой составляющей в металле
The thicknesses de-carbonized layer are within 1–7 mm Additives of boron carbide and silicon carbide reduce the thickness
It was established experimentally that the boron carbide has the best antioxidant properties than silicon carbide in the study circolatorio materials action SiC less effective than B4C
Summary
Был реализован дробный фактор- высушены в сушильном шкафу при ный эксперимент типа 25–1 [3]. Уровни 240 °С для отверждения фенолфорфакторов эксперимента и интервалы их мальдегидной смолы. Водили в колпаковой печи при 980 °С. На лабораторном прессе прессовали образцы в виде цилиндров с диаметром 50 мм. С торца в цилиндре шлако-образующая смесь с основностью (CaO/SiO2) = 1 и содержанием фтора 8 масс. Цилиндры со Таблица 1 Уровни факторов и интервалы их варьирование (план 25–1)