하이드록시 그룹을 지닌 온도민감형 고분자들이 원자전이라디칼중합법(ATRP)과 클릭반응(click reaction)에 의해 합성되어졌다. 고분자들의 분자량과 분자량 분포도는 gel permeation chromatography(GPC)에 의하여 얻어졌고, 고분자들의 분자량은 잘 제어되었으며 분자량 분포도도 낮게 유지되었다. 클릭반응의 효율은 <TEX>$^1H$</TEX> NMR spectroscopy에 의해 얻어졌으며, 높은 효율을 나타내었다. 고분자 사슬 곁가지의 아민 그룹의 종류와, 치환된 알코올 그룹의 종류에 따라 저임계 용액 온도(LCST)의 제어가 가능했다. Thermoresponsive polymers were successfully synthesized by a combination of atom transfer radical polymerization (ATRP) and Cu(I)-catalyzed 1,3-dipolar cycloaddition of azide and alkynes (click chemistry). Poly(2-hydroxyethyl methacrylate) (PHEMA) was synthesized by ATRP, followed by introduction of alkyne groups using pentynoic acid, leading to HEMA-alkyne. Homopolymers having secondary amine groups, tertiary amines with hydroxyethyl and hydroxypropyl groups were synthesized by adding 2-azido-N-ethyl-ethanamine, 2-[(2-azidoethyl)amino]ethanol, and 2-[(2-azidoethyl)amino]propanol, respectively, to the PHEMA-alkyne backbone using click chemistry. Molecular weight (MW), molecular weight distribution (MWD), and click reaction efficiency were determined by gel permeation chromatography (GPC) and <TEX>$^1H$</TEX> NMR spectroscopy. The transmission spectra of the 1.0 wt% aqueous solutions of the resulting polymers at 650 nm were measured as a function of temperature. Results showed that the lower critical solution temperature (LCST) could be easily controlled by the length of the hydroxyalkyl groups.
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.