Abstract
During operation, under cyclic force action, various physical and mechanical processes occur over time in the rail metal: plastic deformation of the rolling surface, the formation of internal and surface cracks, a change in residual stresses, etc. As a result, the mechanical characteristics deteriorate and the performance of the rails decreases. In this work, a microstructural analysis of the cross-sectional surface of two rails with internal cracks - longitudinal and transverse. Rail samples were taken out of service after many years of service. Fractographic analysis of the crack surface and the surrounding material indicates a significant degradation of the physical and mechanical properties of rail steel.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.