AbstractIn this paper, we measured thresholds H _cr of explosive decomposition of thin ( h = 1 mm) samples of PETN-Al composites with densities in the range of ρ = 0.9–1.7 g/cm^3 and variations in the concentration of aluminum inclusions in the range of 0.025–1.0 wt % upon exposure to pulses of a neodymium laser (λ = 1064 nm, 14 ns). For each ρ, inclusion concentrations n _opt, at which the threshold for explosive decomposition of H _cr is minimal, are obtained. The velocities of air shock waves (ASWs) were determined depending on sample density ρ, and the times of the start of explosive decomposition were determined depending on the inclusion concentration. The amplitude (in relative units) and time shift of the maximal pressure of an ASW at the piezodetector are determined depending on sample density. It is concluded that the explosion is governed by the SW mechanism at high densities. As sample ρ decreases, the completeness of the explosion increases, with the most likely mechanism for small ρ being explosive burning. The efficiency of explosive decomposition is higher for samples with lower densities.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.