ВИЗНАЧЕННЯ ТЕХНОЛОГІЧНИХ ПАРАМЕТРІВ ЛАЗЕРНОГО ВИПРОМІНЕННЯ ДЛЯ ОТРИМАННЯ СУБМІКРО- ТА НАНОСТРУКТУР У ЗМІЦНЮВАЛЬНИХ ПОКРИТТЯХ НА СТАЛЯХ

Abstract

Using the previously developed model of theoretical processes in the zone of laser irradiation, where thermal and thermomechanical processes are described, including the influence of crystallization energy and other internal energies during the formation of nanostructures at various temperature levels, further investigation of the thermal and thermomechanical characteristics of different structural steels during the formation of nanostructures on their surfaces using laser irradiation was conducted. To validate the model, temperature fields were determined in the zone of laser irradiation on steel 20 (Fig. 1a) and steel 50 (Fig. 1b), considering both heating and cooling processes. Calculations were performed for heat flux densities and durations of exposure close to those necessary for obtaining nanostructures (500...2000 K) and with temperature rise rates exceeding 10^7 K/s. As a result of calculations using the refined thermal model, temperature distributions at a depth of 1 μm during laser irradiation on steel with different carbon contents (steel 20, 38Х, 50, and У8) at various peak heat flux densities in the surface layer were obtained. A spatiotemporal distribution of temperatures along the radius of the laser spot and over time during laser irradiation with a heat flux density of q=3∙10^8 W/m^2 at a spot radius of 0.1 mm was constructed. Zones of nanostructure formation were identified depending on the heat flux density over the duration of laser irradiation. Theoretical investigations using the updated thermal model confirmed the need to consider the temperature rise rate, as exceeding it increases the likelihood of thermomechanical failure. At the same time, due to insufficient temperature rise rates during laser nanostructure formation in the surface layers of carbon steels, more micro- and sub microstructures are formed.