The effect of thermal barrier coating (TBC) on low cycle fatigue behavior of cast superalloy Inconel 713 LC has been studied at 900 °C. The TBC consisting of a CoNiCrAlY bond coat and a zirconia (ZrO2) top coat stabilized by 8% yttria (Y2O3) was deposited on the gauge section of cylindrical specimens using the atmospheric plasma spray technique. Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment were cyclically strained under strain control with constant total strain amplitude in symmetrical cycle at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of coated and uncoated material were obtained. The stress response of the TBC coated specimens is lower in comparison with the uncoated specimens. Detrimental effect of surface treatment on the Basquin curve is documented. Specimen sectioning and fracture surface observations revealed fatigue damage mechanisms and help to discuss differences in fatigue behavior of the coated and uncoated superalloy.