Epitaxial growth on nickel-plated diamond seeds at high pressure and high temperature (HPHT) was observed with graphite as carbon source. The thickness of the electroplating nickel film which acts as a catalyst/solvent ranges from 54.6 μm to 255.6 μm. The relationship between the Ni film thickness and diamond growth rate is investigated. When the nickel film thickness is from 90 μm to 129 μm, diamond crystals can nearly grow up to three times as large as the original seeds at ∼ 5.8 GPa and ∼ 1460 °C within 14 min. The mechanism of the crystal growth with nickel-plated diamond seeds under HPHT is discussed. The results and techniques might be useful for high quality saw-grade diamonds production and large diamond single crystal growth.