AbstractWe investigated the photoluminescence (PL) properties of regularly arranged N‐polar InN microcrystals with m ‐plane sidewall facets. We observed narrow PL emission at 0.678 eV with a linewidth of ∼14 meV at 4 K and a clear band‐filling effect with increasing excitation power. We also observed a normal red shift of the PL peak energy as large as 51 meV (∼150 nm) with increasing temperature from 4 to 300 K, similar to that observed for non‐degenerated semiconductors. The integrated PL intensity ratio I300K/I4K was measured to be 6.1%. These results indicate that InN microcrystals have a low residual carrier density and excellent optical properties without being adversely affected by surface electron accumulation, despite their relatively high surface area. (© 2012 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)