In this paper, aluminum–doped nano-crystalline zinc oxide (ZnO:Al or AZO) thin films were deposited on fused quartz substrate by pulsed laser ablation at various temperatures. The physical phase and surface morphology were characterized by using X-ray diffraction (XRD) and atomic force microscope (AFM), respectively. The variation of the optical band gap (Egopt) of the films with the temperature was measured through transmittance in UV-VIS wavelength. The results showed that there was a blue shift of Egoptfrom 3.44 eV to 3.62 eV as the growing temperature decreased from 500°C to 200°C. The value of Egoptimmediately recurred from 3.30 to 3.35 eV after a thermal annealing of the samples at 700 °C, inclining to a normal value of bulk zinc oxide. The analyses of XRD and AFM testified that the presence of amorphous phase in the AZO films was the main reason for the blue shift of the optical band gap Egopt.