The standard ISO 14713-1 shows that HDG coatings should protect steel in the corrosive atmosphere C5 for 10–21 years. It was observed that pitting corrosion appears already after 2–3 years on roads and urban infrastructures and both Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) have shown that lead inclusions were present in all such corroded zinc coatings. The laboratory prepared HDG coatings with different amount of lead inclusions were investigated by gravimetric method (after exposure in salt chamber), SEM with EDS, and Glow Discharge Optical Emission Spectrometry (GDOES). The corrosion resistance was analyzed in the polarization tests and local probe techniques. The inclusions could accelerate coating corrosion because lead is cathodic to zinc.