Higher Molecular Weight Of PEG Research Articles

Sodium alginate/polyvinyl alcohol semi-interpenetrating hydrogels reinforced with PEG-grafted-graphene oxide

Semi-interpenetrating polymer network (SIPN) hydrogels composed of sodium alginate/poly (vinyl alcohol), reinforced by PEG-grafted-graphene oxide (GO-g-PEG) were prepared by ionic crosslinking of sodium alginate. The impact of grafted PEG molecular weight with two molecular weights, i.e. 400 and 2000 g/mol, and component composition were studied on the morphology, swelling behavior, mechanical and dynamic properties. SEM observation showed fine dispersion and distribution of GO-g-PEG throughout the hydrogel indicating a good interaction of particles with the components. Our results revealed that although incorporating GO-g-PEG increases the water content, it significantly enhances the mechanical properties, i.e. tensile modulus, elongation at break, and fracture toughness with a more pronounced impact at higher PEG molecular weight. As a result, the tensile modulus and the elongation at break increased by 270 % and 28 %, respectively. The SA/PVA SIPN hydrogels reinforced with the GO-g-PEG exhibit a non-linear elastic behavior with a toe at low strains. This behavior is attributed to the unique structural features of SIPN hydrogels and the orientation of GO-g-PEG particles with proper interaction with the components. The small amplitude oscillatory shear was also performed to further study the impact of SA, PVA, and GO-g-PEG compositions on the microstructure of hydrogels.

Environmental usefulness of PLA/PEG blends for controlled‐release systems of soil‐applied herbicides

ABSTRACTBlends consisting of biodegradable polylactide (PLA) and poly(ethylene glycol) (PEG) were investigated for their usefulness as an environmentally friendly herbicide formulation with prolonged activity. The aim of this study was to evaluate the release rate of selected soil‐applied herbicides from the PLA/PEG blend containing PEG of various molecular weights and to assess the phytotoxicity of the PEGs according to OECD 208 guidelines. The release rate of immobilized herbicides was correlated with degradation of the blends used. The progress of PLA/PEG blend degradation in water, soil, and activated sludge was estimated by sample weight loss, changes in blend composition, and microscopic observations of the blend surfaces during the experiment. The proposed formulation of the immobilized herbicide in a blend consisting of slowly biodegradable PLA and water‐soluble PEG provides the possibility to release the herbicides for a relatively long time, for approximately six months, which is a demand of weed management. The effect of PEGs on plant growth and development was dependent on both their concentration and molecular weight. With a higher concentration in soil and a higher molecular weight of PEG, a more harmful effect on plants was noticed. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 47856.

Synthesis and properties of novel photocrosslinkable aromatic-aliphatic liquid crystal copolyesters based on poly(ethylene glycol) and cinnamic acid

ABSTRACTFirstly, PEGn-TA monomers with carboxyl functional groups were synthesised by terephthalic acid (TA) and poly(ethylene glycol) (PEG) with molecular weight of 200, 400 and 600. Then, photocrosslinkable thermotropic liquid crystal copolyesters derived from PEGn-TA, 4,4ʹ-biphenol, 4-hydroxy-cinnamic acid and 4-hydroxy-benzoic acid were successfully obtained by Vilsmeier adduct solution polymerisation method. Influence of PEG molecular weight on thermal behaviour, liquid crystal mesophase, hydrophilicity, structure and photoactivity were investigated by various measurements. Experimental results indicated that all copolyesters showed nematic mesophase textures, relative low melting temperatures, and two glass transitions as well as better hydrophilicity were observed for those contained higher PEG molecular weight. Photocrosslinking rate was increased first and then decreased due to effect of flexible PEG moieties. The resulted copolyesters with liquid crystal behaviour, excellent hydrophilicity and photoactivity could be potentially used as biomaterial.

Air-Water Interfacial Properties of Chloroform-Spread versus Water-Spread Poly((d,l-lactic acid- co-glycolic acid)- block-ethylene glycol) (PLGA-PEG) Polymers.

Polymers at fluid interfaces are used for a number of applications that include coatings, electronics, separation, energy, cosmetics, and medicines. Here, we present a study on an amphiphilic block copolymer, poly((d,l-lactic acid- co-glycolic acid)- block-ethylene glycol) (PLGA-PEG), at the air-water interface. PLGA-PEG at the air-water interface prepared by using an organic spreading solvent exhibits an extremely high surface pressure without the occurrence of desorption, making it an attractive candidate for a variety of uses in the areas mentioned above. The origin of this high surface pressure increase was shown to be due to the glass transition of the PLGA segments. The temperature at which this glass transition occurs for the PLGA segments of PLGA-PEG at the air-water interface was measured to be about 290 K by thermodynamic analysis based on the two-dimensional Maxwell relations. However, from an applications standpoint, spreading by an organic solvent greatly limits its scope of feasible uses. To explore the possibility of maintaining the excellent surface mechanical properties of the PLGA-PEG at the air-water interface while not using an organic solvent, we investigated the air-water interfacial properties of water-spread PLGA-PEG. When spread with water, it was shown that the initial micelles that form in the aqueous spreading solution remain intact even after being spread onto the air-water interface. Due to this different morphology, the surface pressure and monolayer stability were greatly reduced for the water-spread PLGA-PEG at the air-water interface. We used the Daoud and Cotton's blob scaling model to describe the desorption process of the water-spread PLGA-PEG at the air-water interface. From the scaling concept, it was shown that with higher PEG molecular weight and larger micelle size, the adsorption energy of the water-spread PLGA-PEG to the air-water interface was increased.

Soft hydrogels from tetra-functional PEGs using UV-induced thiol–ene coupling chemistry: a structure-to-property study

In this work, photo-induced thiol–ene coupling (TEC) was used to produce well-defined poly(ethylene glycol) (PEG)-based hydrogels. PEGs of four different molecular weights (2k, 6k, 10k, and 20k) were functionalized with G1-allyl dendrons using anhydride chemistry to produce tetra-functional TEC crosslinkable PEGs. The tetra-functional PEGs were subsequently crosslinked with a tri-functional thiol in ethanol to form hydrogels. The synthesized hydrogels were characterized with respect to swelling behaviour, rheological properties and hydrolytic degradation. It was found that the molecular weight of the PEG chain greatly influences the final properties of the hydrogel, where a higher molecular weight of PEG gives an increased weight swelling ratio from 240% for PEG-2k hydrogels to 1400% for PEG-20k hydrogels, as well as decreased elastic moduli, with Young's moduli ranging from 106 MPa to 6 MPa, for PEG-2k and PEG-20k hydrogels, respectively. It was also found that the hydrolytic stability in alkaline conditions (pH 10) decreased when the molecular weight of PEG in the hydrogels increased.

Synthesis, characterization, in vitro and in vivo evaluation of PEGylated oridonin conjugates

Oridonin (ORI), a diterpenoid compound with promising antitumor activity, was proved to possess potent antileukemia efficacies in vitro and in vivo recently. However, the development and application of ORI was limited by its poor solubility and rapid plasma clearance. The purpose of this study was to solve these problems. PEGylated oridonin linked with succinic acid (SA) as spacer moiety (PEG-SA-ORI conjugate) was synthesized. mPEG amines with four specifications of molecular weight (MW) were utilized. All polymeric conjugates showed satisfactory aqueous solubility and in vitro studies implied that the drug solubility and release features of conjugates were relevant to PEGs. The drug solubility increased more when the MW of PEG was lower, while more significant sustained-release effect was shown with higher PEG MW. Moreover, the release behaviors of conjugates showed a pH-sensitive property. In vivo pharmacokinetic studies demonstrated that the elimination half-life was prolonged in comparison with ORI solution. PEGylation could be a promising method to obtain better efficacy in the field of drug delivery system.

Investigating the Uni-HEUR thickener performance considering hydrophilic segment length

Hydrophobically modified ethoxylated urethane models were synthesized through hydrophobic modification of poly(ethylene glycol) (PEG) by octadecyl isocyanate. Their structure consisted of linear water-soluble PEG backbones of number average molecular weight 6000 and 10,000 which end capped by aliphatic C 18 chains attributed to octadecyl isocyanate. The behavior of thickener models was studied in both DDI (double distilled water) and a water-based resin of vinyl acrylic copolymer emulsion. The steady and oscillatory shear viscosity of both aqueous and resin systems containing the thickener models were determined. The result for constant hydrophobic length (C 18) showed that the associative thickener with higher molecular weight of PEG or longer hydrophilic length presents superior rheological properties. The concentration of thickeners can influence the phase behavior of the systems in such a way that for smaller length of the thickener the interconnection among micelles and the emulsion particles exist at equilibrium (concentrations of 2–3 wt%). However, for the higher-length associative polymer, it disappears upon a concentration rise to 4 wt%.

Anti-atherosclerotic peptide delivery from a photocrosslinkable biodegradable network

A water-soluble, 19-mer peptide fragment of serum amyloid A called MFFD is being examined as a possible treatment for atherosclerosis. As a means of administering this drug in a sustained fashion through subcutaneous implantation, a biodegradable network formulation was prepared. The formulation consisted of 1000 and 4000 Da α,ω-diacrylate oligo( d, l-lactide)- b-poly(ethylene glycol)- b-oligo( d, l-lactide) (DLPEGDLDA) copolymerized with 2700 and 5000 Da ω,ω,ω-triacrylate star-poly(ɛ-caprolactone- co- d, l-lactide) using UV irradiation. The influence on the network properties and degradation rate of the network on the amount and type of DLPEGDLDA copolymerized with the two different molecular weight ASCPs were examined in vitro. The networks degraded by bulk hydrolysis at a rate controlled primarily by the molecular weight of the ASCP used. Nevertheless, all the networks were completely degraded within 16 weeks. The MFFD was released in a diffusional manner at a rate influenced by the degree of swelling of the network and the molecular weight of the ASCP used; using an ASCP of a lower molecular weight for a given DLPEGDLDA resulted in a slower release rate. The degree of swelling of the networks was controlled solely by the nature of the PEG used in preparing the DLPEGDLDA, with greater swelling observed with higher PEG molecular weight and for greater amounts of PEG incorporation. The MFFD was not degraded during the photocrosslinking reaction or by potential acidic degradation products that may have accumulated within the device. This formulation provides a means of achieving a desirable release rate from a degradable, water-swellable network through selection of ASCP molecular weight and DLPEGDLDA composition.

A Novel Method for the Synthesis of the PEG‐Crosslinked Chitosan with a pH‐Independent Swelling Behavior

In this study, a simple method was developed to crosslink chitosan using poly(ethylene glycol) (PEG) with different molecular weights. Crosslinking of chitosan was confirmed by various spectral analyses. The differential scanning calorimetric (DSC) study indicated that the rigid crystalline structure of chitosan was decreased after crosslinking with PEG. The PEG-crosslinked chitosan (PEG-Ch) showed a pH-independent swelling behavior: swelled in both the simulated stomach (pH 1.1) and intestinal (pH 7.4) solutions. The swelling ratio of PEG-Ch increased significantly with a higher molecular weight of PEG used. In contrast, chitosan dissolved completely in a simulated stomach solution and showed a comparatively less swelling in a simulated intestinal solution. Thus, the prepared PEG-Ch could be a better biomaterial than chitosan in the development of orally sustained drug-delivery devices.

Clonazepam release from bioerodible hydrogels based on semi-interpenetrating polymer networks composed of poly(ε-caprolactone) and poly(ethylene glycol) macromer

Poly(ethylene glycol)(PEG) macromers terminated with acrylate groups and semi-interpenetrating polymer networks (SIPNs) composed of poly(ε-caprolactone)(PCL) and PEG macromer were synthesized to obtain a bioerodible hydrogel. Polymerization of PEG macromer resulted in the formation of cross-linked gels due to the multifunctionality of macromer. Glass transition temperature ( T g) and melting temperature ( T m) of PEG networks and PCL in the SIPNs were inner-shifted, indicating an interpenetration of PCL and PEG chains. Water content in the SIPNs increased with increasing PEG weight fraction due to the hydrophilicity of PEG. The amount of clonazepam (CNZ) released from the SIPNs increased with higher content in the SIPNs, lower drug loading, lower concentration of PEG macromer during the SIPNs preparation, and higher molecular weight of PEG. In particular, a combination with low PEG content and low CNZ solubility in water led to long-term constant release from these matrices in vitro and in vivo.

Albumin release from bioerodible hydrogels based on semi-interpenetrating polymer networks composed of poly( ϵ-caprolactone) and poly(ethylene glycol) macromer

Poly(ethylene glycol) (PEG) macromers terminated with acrylate groups and semi-interpenetrating polymer networks (SIPNs) composed of poly( ϵ-caprolactone)(PCL) and PEG macromer were synthesized and characterized to obtain a bioerodible hydrogel that can be used for albumin delivery. Polymerization of PEG macromer resulted in the formation of cross-linked gels due to the multifunctionality of macromer. Glass transition temperature ( T g) and melting temperature ( T m) of PEG network and PCL in the SIPNs were inner-shifted, indicating an interpenetration of PCL and PEG chains. Water content in the SIPNs increased with increasing PEG weight fraction due to the hydrophilicity of PEG. The amount of albumin released from the SIPNs increased with higher PEG content in the SIPNs, higher drug loading, lower concentration of PEG macromer during the SIPNs preparation, and the higher molecular weight of PEG. The degradation rate of the SIPNs gels in vitro increased with increasing of PEG weight fraction.

Synthesis and Enzymatic Degradation of Nylon 66 Copolymers with Poly(Ethyleneglycol)s

Abstract Nylon 66 (N66) copolymers were prepared by melt polycondensation of adipic acid and hexamethylenediamine with 5–80 mol% poly(ethylene glycol) (PEG), where the molecular weight (MW) of PEG was 200–1000. The reduced specific viscosity of the copolymers was increased by the copolymerization. The crystallinity and melting temperature (T m) of N66 components decreased with increasing PEG content, but T m depression of copolymers at the same mole content decreased with increasing MW of PEG, suggesting that the copolymer structures are not of the random type but of the block type at the higher MW of PEG. The water absorption increased with increasing PEG content, and its increase was much higher at the higher MW of PEG. The enzymatic degradation was estimated by the weight loss of copolymer films in the buffer solution with and without a lipase at 37°C. The weight loss was enhanced appreciably by the presence of a lipase, and increased abruptly at higher PEG content, which was correlated to water absorp...