Statement of problemPolyetherketoneketone (PEKK) is a high-performance polymer gaining popularity in dentistry for the fabrication of crowns, fixed partial dentures, removable partial denture frameworks, and frameworks for implant-supported fixed complete dentures. Despite a lack of performance data, lithium disilicate crowns have been bonded to retentive elements in PEKK frameworks. PurposeThe purpose of this in vitro study was to compare the bond strengths and flexibility of lithium disilicate to PEKK or zirconia. Material and methodsForty-five PEKK, 15 zirconia, and 60 lithium disilicate beam-shaped specimens (12.5×2×2 mm) were fabricated. The ends of the PEKK beams were subjected to 3 different surface treatments before the application and light polymerization of a primer: 50-μm aluminum oxide airborne-particle abrasion, nonthermal air plasma, and argon-oxygen plasma. The zirconia specimen bonding surfaces were prepared with 50-μm aluminum oxide airborne-particle abrasion and the application of primer. Lithium disilicate specimens were etched with 4.5% hydrofluoric acid, and primer was applied. The lithium disilicate specimens were luted with an adhesive resin cement to the PEKK and zirconia specimens by using light-activated and chemically activated polymerization. Fifteen monolithic specimens of PEKK, lithium disilicate, and zirconia (25×2×2 mm) were also fabricated. All specimens were incubated overnight in 100% humidity before testing. Bonded and monolithic specimens were loaded in a universal testing machine, and 4-point bend tests were conducted until failure (n=15). The flexural modulus and strength were calculated and statistically analyzed with 1-way analysis of variance and Student-Newman-Keuls post hoc tests (α=.05). ResultsAll bonded specimens failed at the adhesive interface. The zirconia-lithium disilicate bond strength was approximately twice that of the strongest group of PEKK (airborne-particle abrasion group) bonded to lithium disilicate (42 ±12 MPa and 24 ±13 MPa, respectively) and was approximately 9 times more rigid (71 ±19 GPa and 8 ±2 GPa, respectively). Monolithic PEKK fractured at 238 ±22 MPa, monolithic zirconia at 771 ±128 MPa, and monolithic lithium disilicate at 173 ±26 MPa. Monolithic PEKK was approximately 30 times more flexible than monolithic zirconia (6 ±1 GPa and 178 ±16 GPa, respectively). All values were statistically significantly different (P<.05), except for the bond strength between lithium disilicate and PEKK treated with airborne-particle abrasion and nonthermal air plasma and the flexural moduli of PEKK to lithium disilicate. ConclusionsBond strength between PEKK and lithium disilicate was significantly weaker than that between zirconia and lithium disilicate. Monolithic PEKK was significantly more flexible than monolithic zirconia.