Abstract
Zinc incorporation by post-growth metalorganic vapor phase diffusion (MOVPD) is used to achieve high p-doping, which is desirable for the fabrication of photodiodes. Diethylzinc (DEZ) is used as precursor and Zn is diffused into InP and InAs0.6P epitaxial layers grown by low pressure metalorganic vapor phase epitaxy (MOVPE) on different substrate orientations, enabling the investigation of the dislocation density on the Zn incorporation. Diffusion depths are measured using cleave-and-stain techniques, resistivity measurements, electrochemical profiling, and secondary ion mass spectroscopy. High hole concentrations of, respectively, 1.7 1019 and 6 1018 cm−3, are obtained for, respectively, InAs0.60P and InP. The diffusion coefficients are derived and the Zn diffusion is used for the fabrication of lattice-mismatched planar PIN InAsP/InGaAs photodiodes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.