YSZ films fabricated by a spin smoothing technique and its application in solid oxide fuel cell

Abstract

A dense single-layer YSZ film has been successfully fabricated by a spin smoothing method. Followed by a simplified slurry coating, an additional spin smoothing process was conducted to obtain a thinner and smoother film. By employment of high-viscosity slurry including high YSZ content, the film has a suitable thickness by a single coating cycle. With Sm 0.2Ce 0.8O 1.9 (SDC)-impregnated La 0.7Sr 0.3MnO 3 (LSM) cathode and porous NiO–YSZ anode, single solid oxide fuel cell (SOFC) based on an 8-μm-thick YSZ film was obtained. Open-circuit voltage (OCV) of the cell was 1.04 V at 800 °C, and maximum power densities were 676, 965 and 1420 mW cm −2 at 700, 750 and 800 °C, respectively, using H 2 at a flow rate of 40 mL min −1 as fuel and ambient air as oxidant. The power density could be increased to 1648 mW cm −2 at 800 °C when the flow rate of H 2 was enhanced to 200 mL min −1.