Abstract
Friction stir spot welding (FSSW) was applied to make lap-joints of 5052 rolled (5052-R) aluminum alloys. The resulting microstructural observation, microhardness, tensile shear failure load and failure morphologies are reported, including a brief look into failure behaviors in the present study. The metallurgical bonded TMAZ region with a plastic metal flow is obviously created around the probe, and the microhardness is significantly increased at the TMAZ region for FSSW-joined 5052 aluminum alloys. The FSSW lap-joints with an obvious metallurgical bonded TMAZ region generally display a higher failure load and ductile failure morphologies with dimples fracture. In addition, the failure load of FSSW lap-joints was increased with increasing the probe penetration depth and the welding time. Based on the data fluctuation of tensile shear failure load, the Weibull model provided a statistical analysis method for assessing the minimum failure, the failure mechanism and the joining reliability for the FSSW lap-joints. Through the statistical analysis of the Weibull distribution function, FSSW-joined aluminum alloys with a wear-out failure model are recognized as reliable lap-joints for further engineering application. [doi:10.2320/matertrans.MRA2008341]
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.