Abstract
Graphene oxide (Go) has excellent mechanical properties, corrosion resistance, solid lubricant properties, and no biotoxicity. In this study, CoCrFeNiMn coating adding 2 wt.% single layer of Go was prepared by laser cladding (LC) on the surface of Q235B. To explore the possibilities of Go as a reinforced powder. It was found that the alcohol stirring method could uniformly mix Go with HEA powder and would not destroy its microstructure. The main phase composition of the coatings does not change, but peaks of oxides and carbides were generated in the coatings. The carbide and oxide generation in the coating was demonstrated by EDS spot scanning. The addition of Go increased the microhardness of the coating by 51.33%. The average coefficient of friction (COF) of the HEA/Go coating decreased by 16%, the wear rate decreased by 82.05%, and the wear weight loss decreased by 77.26%. Improvement of the wear properties is mainly attributed to the generation of oxide film during friction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.