Abstract
Abstract The silicon-containing diamond-like carbon (DLC) films have been deposited on SKD61 steel by r.f. PECVD (plasma-enhanced chemical vapor deposition). A pin-on-disk wear test with a higher normal load, 30 and 40 N, was conducted to investigate the wear behavior of the DLC films. Various structures of the films obtained by different deposition conditions lead to different wear lives of the DLC-coated steels. A DLC film with small amount of silicon addition has a lower friction coefficient (0.01) than an undoped film (0.1). Raman analysis showed that in the wear test, graphitization of the pure DLC film occurs at the initial stage, whereas for the silicon-containing DLC film, graphitization of the wear debris or transferred film was not observed after the wear test, which indicates that the silicon-containing DLC film exhibits a better thermal stability than the pure DLC film. The lower friction coefficient value of silicon-doped DLC may be due to the formation of SiO 2 that might arise from the contamination in the deposition system or oxidation in processing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.