Abstract
Aliphatic epoxy composites with multifunctional polyhedral oligomeric silsesquioxane (POSS) ((C6H5CHCHO)4(Si8O12)(CHCHC6H5)4) nanophases (epoxy/POSS 95/5 and 75/25) and epoxy blends with the prepolymer of ladderlike polyphenylsilsesquioxane (PPSQ) (95/5, 90/10, and 85/15) were prepared by solution casting and then curing. These composites and blends were studied by dynamic mechanical thermal analysis (DMTA) and mechanical testing. The POSS units incorporated into the epoxy network are well dispersed in the composite, probably on the molecular scale, even at high POSS content (25 wt %) based on TEM observations. However, the aliphatic epoxy/PPSQ blends exhibit good miscibility only at low PPSQ content (≤10 wt %). Phase separation was clearly observed when the PPSQ content was 15%. Incorporation of the POSS macromer into this epoxy network by curing at upper temperatures of 120 and 150 °C broadened the temperature range of glass transition of the resulting composites but has almost no influence on their Tg ...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.