Abstract
In this paper, the calcium-doped nickel-zinc nano-ferrites [Ni0.5Zn0.5CaxFe2-xO4; x = 0.00, 0.10, and 0.30] were prepared using the chemical co-precipitation synthesis route and studied for switching field high-frequency device applications. The structural analysis has been completed by analyzing X-ray diffraction (XRD) patterns. The Rietveld refined XRD patterns confirmed the formation of cubic spinel structure of Ca2+ substituted nickel-zinc ferrites. The detection of metal-oxygen bonds present at A and B lattice sites has been unveiled by Fourier transform infrared (FTIR) spectroscopy. The morphological studies obtained through FESEM (Field emission scanning electron microscopy) analysis showed a reduction in the particle size from 70 nm to 53 nm when the concentration of Ca2+ ions in Ni-Zn ferrites was increased. Energy dispersive spectra (EDS) confirmed the presence of elements present in the prepared composition. The structure of a cubic spinel-shaped unit cell has been verified from three active prominent Raman modes (A1g, A2g, and T2g). Diffuse-reflectance spectroscopy (DRS) exhibits the increment in the bandgap values (from 1.55 eV to 1.63 eV) which helps fabricate highly efficient photovoltaic devices. The ferroelectric measurements yielded a rise in polarization values from 1.461 μC/cm2 to 18.228 μC/cm2 for 10 % Ca2+ ion substitution. The tangent loss values declined from 24 to 3 in Ni-Zn ferrites upon substituting Ca2+ ions. The Vibrating sample Magnetometer (VSM) technique found the increment in the saturation magnetization (Ms) values from 34.724 emu/g to 54.662 emu/g on substituting up to 30 % Ca2+ ions in Ni-Zn ferrites. These obtained results support the material in switching field distribution for high-frequency applications. The results exhibited that the prepared samples can be applicable for switching devices, filters, and microwave absorption devices. The results revealed the maximum frequency between 12 and 18 GHz which is useful for Ku band absorption.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.