Abstract
The microstructure evolution and oxide film behavior in ultrasound-assisted transient liquid phase (U-TLP) bonding of Mg alloy were investigated by applying different ultrasonic time at 460 °C with brass interlayer in air. The results indicated that with increasing ultrasonic time, brass interlayer disappeared gradually and the Mg-Cu-Zn eutectic compounds were formed. The eutectic compounds in the joint decreased as the ultrasonic time increased further. The oxide removal process was divided into four steps. Continuous oxide film at the interface was partially fractured by ultrasonic vibration, and then suspended into liquid by undermining eutectic reaction. After that, the suspended oxide film was broken into small oxide fragments by ultrasonic cavitation effect, which was finally squeezed out of the joint by ultrasonic squeeze action. In addition, the mechanical properties of the joints were investigated. The maximum shear strength of the joint reached ∼105 MPa, which was 100% of base metal.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.