Abstract
Ultrasonic additive manufacturing (UAM) was applied to fabricate laminated carbon steel structures. The feasibility of UAM to manufacture low-alloy carbon steel samples was proven. Interface investigation of the UAM parts was conducted by SEM, EBSD and TEM analysis. Multiple defects at the interfaces of the as-printed parts were observed. In order to improve the structural homogeneity and mechanical properties of the parts, spark plasma sintering (SPS) and hot isostatic pressing (HIP) post-treatments were applied. As a result, after both treatments, interface defects were healed and the shear strength of the welding interfaces was significantly improved. Treatment by SPS apparatus showed higher shear strength improvements as compared to the HIP-treated specimens.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.