Abstract
The linear and mass ablation rates of Ti2AlC ceramics under an oxyacetylene flame at a temperature up to 3000°C were examined by measuring the dimensions and weight change of the ablated samples. The linear ablation rate was decreased from 0.14μms−1 for the first 30s of the ablation to 0.08μms−1 after 180s. Ti2AlC ceramics gained small amounts of weight upon ablation, which is attributed to the formation of oxidation products on the ablated surface. The ablation surface exhibits a two-layer structure: an oxide outer layer, consisting mainly of α-Al2O3 and TiO2 and some Al2TiO5, and a porous sub-surface layer containing Ti2Al1−xC and TiCxOy. With increasing ablation time, the content of TiO2 and Al2TiO5 in the outer layer increased, and more pores developed in the sub-surface layer. The thermal oxidation of Ti2AlC under the flame and scouring of the viscous oxidation products by high-speed flow of gas torch are the main ablation mechanisms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.