Abstract
Tungsten (W) coating on fusion candidate V-4Cr-4Ti (NIFS-HEAT-2) substrate was demonstrated with plasma spray process for the purpose of applying to protection of the plasma facing surface of a fusion blanket. Increase in plasma input power and temperature of the substrate was effective to reduce porosity of the coating, but resulted in hardening of the substrate and degradation of impact property at 77 K. The hardening seemed to be due to contamination with gaseous impurities and deformation by thermal stress during the coating process. Since all the samples showed good ductility at room temperature, further heating seems to be acceptable for the vanadium substrate. The fracture stress of the W coating was estimated from bending tests as at least 313 MPa, which well exceeds the design stress for the vanadium structure in fusion blanket.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.