Abstract
Bulk YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// material with single-domain grains up to 35 mm in diameter was prepared by a modified melt-texturing process. The pinning properties were improved by chemical doping of Zn on Cu plane sites resulting in a well pronounced peak effect in the field dependence of the critical current density. Trapped fields of more than 1.1 T at 77 K have been obtained in a zinc-doped YBCO disk of only 27 mm in diameter. Higher trapped fields are observed at lower temperatures due to the increasing critical current density, however, at temperatures between 50 and 20 K, the trapped field is limited by the mechanical properties. Using a bandage made of steel, very high trapped fields were achieved in the 1 mm gap between two YBCO disks. Trapped fields up to 14.4 T were found at 22.5 K in such minimagnets containing silver precipitates, whereas the trapped fields of zinc-doped minimagnets reached values of 11.2 T at 47 K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.