Abstract
ABSTRACTPolylactide (PLA)/polyurethane (PU) composites were prepared by reactive blending method with in situ formation of PU particles via the reaction between polyester polyol (PPG) and toluene‐2,4‐diisocyanate (TDI). The interfacial compatibility and adhesion between the PLA and PU phases were greatly improved by the reaction of the terminal hydroxyl groups of PLA and NCO groups of TDI forming graft copolymer, as confirmed by FTIR spectroscopy. The elongation at break and notch impact strength of PLA/PU composites increased considerably with increasing PU content, and the tensile strength of PLA/PU composites decreased slightly compared with that of pure PLA. Upon addition of 12 wt % PU, the elongation at break and notch impact strength increased to 175.17% and 10.96 kJ/m2, respectively, about 27 times and 5.4 times greater than the corresponding values for the pure PLA. The tensile strength decreased only slightly to 48.65 MPa. The excellent interfacial adhesion, the dispersed PU elastomeric particles acting as stress concentration areas, and the triggering of large matrix shear yield as well as many fibrils by internal cavitation were the main mechanical toughening mechanisms. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 44383.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.