Abstract
Mg2Si1−x Sn x -system solid solutions are ecofriendly semiconductors that are promising materials for thermoelectric generators in the middle temperature range. To produce a thermoelectric device, high-performance p- and n-type materials must be balanced. In this paper, p-type Mg2.00Si0.25Sn0.75 with Li and Ag double doping was prepared by the liquid–solid reaction method and hot-pressing. Effects of Li and Ag double doping on thermoelectric properties were investigated in the temperature range from room temperature to 850 K. All sintered compacts were identified as single-phase solid solutions with anti-fluorite structure. The carrier concentration increased with the double doping. The temperature dependence of resistivity of the double-doped samples was similar to that of a metal. The seebeck coefficient increased with temperature to a maximum value and then decreased in the intrinsic region. Thermal conductivity decreased linearly with increasing temperature, reaching a minimum near the intrinsic region, and then increased rapidly because of the contribution of the bipolar component. The dimensionless figure of merit reached 0.32 at 610 K for Mg2.00Si0.25Sn0.75 double-doped with Li-5000 ppm and Ag-20000 ppm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.