Abstract
Thermoelectric generator is expected as an independent source, an energy converter for co-generation with Refuse Derived Fuel (RDF) and so on. Thermoelectric materials were required high Seebeck coefficient, low electrical resistivity and low thermal conductivity. Thermoelectric oxides are suitable at the high temperature range because of chemical stability. Authors focus attention on Aurivillius compounds. The Aurivillius compounds consist of Perovskite layers and Bi-O layers. It is expected that nano-layered structure shows high Seebeck coefficient due to the quantum confinement of electron in Perovskite layers. It was reported that the Seebeck coefficient of Aurivillius phase Bi2VO5.5 was high value of -28.3 mVK-1 at 1010 K, and the electrical resistivity of the one was also high value of 0.033 Ωm at 1010 K. We investigated about element substitution effects at V site on thermoelectric properties. Bi2V1-xMxO5.5 (M=Cu, Cr, x=0, 0.05, 0.1, 0.2) were prepared by solid-state reaction and hot pressing. From the results of the electrical resistivities and the Seebeck coefficients, Cu and Cr behaved as acceptor to Bi2VO5.5. Cr was effective for reducing the thermal conductivity of Bi2VO5.5. The maximum value of dimensionless figure of merit for Bi2VO5.5 was 0.06 at 910 K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.