ABSTRACTThe Ti-Ni-Cu shape memory alloy by elemental powders was fabricated by means of a pulse-current pressure sintering method that can produce high-density sintered compacts in a very short sintering time. The fabrication conditions of Ti-Ni-Cu alloy and the influence of Cu content in Ti-Ni-Cu alloy on the tensile properties and thermo-mechanical characteristics were investigated. The relative density of the as-sintered compacts was around 97% at any Cu content. The microstructure, tensile properties and thermo-mechanical characteristics of the as-sintered compacts were improved greatly by performing a solid solution heat-treatment. The yielding behavior due to the stress-induced martensite in stress-strain curves of the alloy took place after elastic deformation at any Cu content. The deformation resistance of the alloys changed with Cu content, and it was lowest around 9at% in Cu content. The tensile strength and elongation of the alloy with Cu content around 9at% were more than 400 MPa and 6%, respectively. It was found that the thermo-mechanical behavior of the alloy becomes stable by performing cyclic deformation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.