Abstract
Thin metallic coatings (0.3 and ) were deposited by magnetron cosputtering on bare and on 100 h preoxidized ZMG232L stainless steel substrates for application as protective coatings for solid oxide fuel cells (SOFCs) interconnects. The coatings on bare steel were oxidized for different times of up to 101 h at in ambient air. After 1 h heat-treatment, the metallic films had already converted to oxide with a spinel structure. With increasing oxidation time, a phase was also detected, independent of the thickness of the coatings. This phase formation was attributed to Mn ion enrichment in the coating. Cr diffusion and stresses in the thin coatings were also observed. Bare steel samples were also preoxidized for different durations to determine a suitable oxidation time to form a stable oxide scale on their surface. Steel samples preoxidized for 100 h and coated with were subjected to time-dependent area specific resistance (ASR) measurements for 500 h. The ASR values obtained were 15 and for the substrate coated with 0.3 and , respectively. Also, no phase was present, and no Cr diffusion was detected in the thicker coating.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.