Abstract
Ti and Ni sulfides were formed on the surface of Ti-Ni alloys by isothermal annealing at various sulfur pressures, and then microstructures of the surface sulfide layers were investigated by means of scanning electron microscopy and X-ray diffractions. Morphology of sulfurized surface changed from granular shape to porous shape at the sulfur pressure of 80 kPa, which is related to the change in sulfide from NiS1.97 to NiS. Two-layered sulfide was observed in which the inner layer was mainly Ti8.2S11 , and the outer layer was a mixture of NiS1.97 and NiS. The discharge curve of the Ti and Ni sulfides cathode formed on the Ti-Ni current collector at the first cycle showed a plateau voltage of 1.6 V, and the discharge capacity was found to be about 530 mAh/g-NiS1.97.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.