Abstract
The influence of the preparation method of NiAl2O4 binders on their thermal stability was studied. For this purpose, the reactivity of two different NiAl2O4 binders with CO as fuel was studied in a fixed bed reactor device. Successive oxidation–reduction cycles were performed on the two binders to study their reactivity with the fuel and their structural modifications as cycles proceed. Results reveal that binders are not inert in reducing atmosphere; they both react with the fuel to produce CO2. The total reduction capacity (TRC) of the first binder (B1, synthetized by pyrolytic pulverization) increases during the first cycles and levels off after 20 cycles. However, the TRC of the second binder (B2, synthetized by calcination of a mixture of Ni(OH) and γ-Al2O3), increases progressively and reaches a maximum after 80 cycles. The growing amount of available oxygen in the binders leads both binders to structural modifications. X-ray Diffraction studies performed on fresh and aged binders presented a shift of the peaks related to NiAl2O4. Moreover, quantitative X-ray Diffraction studies and Temperature Programmed Reduction measurements were performed in order to quantify the NiO present in each binder before and after oxidation–reduction cycles. These experiments revealed the presence of NiO in fresh binders due to the preparation method, and an increase of this amount after oxidation–reduction cycles. Therefore, NiAl2O4 in the binder is progressively decomposed producing NiO and Al2O3. Finally, the decomposition of the binder NiAl2O4 as cycles proceed was also observed in studies performed on the oxygen carrier NiO/NiAl2O4. This work showed that the binder reacts with the fuel and therefore it can contribute to the modification of the oxygen carrier reactivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.