Abstract
Thermogravimetric (TG) and differential thermal analysis (DTA) curves of methyltributylammonium smectite (MTBAS), methyltrioctylammonium smectite (MTOAS), and di(hydrogenatedtallow)dimethylammonium smectite (DHTDMAS), and also corresponding sodium smectite (NaS) and tetraalkylammonium chlorides (TAAC) were determined. The TAACs was decomposed exactly by heating up to 500°C. The adsorbed water content of 8.0% in the pure NaS was decreased down to 0.2% depending on the size of the non-polar alkyl groups in the tetraalkylammonium cations (TAA+). The thermal degradation of the organic partition nanophase formed between 2:1 layers of smectite occurs between 250–500°C. Activation energies (E) of the thermal degradations in the MTBAS, MTOAS and DHTDMAS are 13.4, 21.9, and 43.5 kJ mol−1, respectively. The E value increases by increasing of the interlayer spacing along a curve depending on the size of the alkyl groups in the TAA+.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.