Abstract
Target materials in this experiment were FePt alloy nanoparticles with face‐centered tetragonal structure, narrow size distribution, and the size of 6–8 nm. This type of materials was expected to have high recording‐density of 1 Tbit/inch2 with high magnetic anisotropy. In this study, a detailed investigation was carried out to understand the reduction characteristics of Pt complexes, and FePt alloy nanoparticles with diameters larger than 6 nm was try to synthesize. For the synthesis of Pt nanoparticles by using polyol process, three kinds of Pt complexes, namely, H2PtCl6, Pt(EDTA), and Pt(acac)2 was used. The size of Pt metal nanoparticles was only few nm in the case of single Pt complex, while it was increased to 7–10 nm in the case of mixed Pt complex and adjusting the reaction temperature increasing ratio. FePt alloy nanoparticles with the diameter of 7–8 nm, distorted shape, and narrow size distribution were successfully synthesized. However, composition ratio of the particle was Fe12–21Pt79–88, nev...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.