Abstract
Three polypropylene samples (1-3) were synthesized with a 4th generation Ziegler-Natta catalyst in the presence of cyclohexyldimethoxymethylsilane (donor c), dicyclopenthyldimethoxysilane (donor d) and diisopropyldimethoxysilane (donor p), respectively, as external electron donors. The physical properties of the synthesized polypropylenes were determined. For samples 1 to 3, Successive self-nucleation and annealing (SSA) and Fourier transform infrared spectroscopy (FT-IR) analyses indicated that the relative content of the fraction with high isotacticity and regularity in conformational structure decreased in contrast with the fraction of low isotacticity and low uniformity in stereo-defect distribution from sample 1 to 3. The results demonstrated that the longer the isotactic sequence length and the less uniform the stereo-defect distribution, the greater the conformational order. Deconvolution of the molecular weight distribution curves indicated that the stability of the active centers increased from samples 1 to 3, but the participation of stereo-specefic active centers in the polymerization decreased. DMA tests showed that samples 3 and 1 had the highest damping ability and storage modulus, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.