Abstract
The phase evolution mechanism in Fe(Se, Te) system during sintering was investigated with step-by-step heat treatment process. It was noticed that the diffusion processes between Fe and Se (Te) as well as that between Se and Te were both very important to the formation of superconducting Fe(Se, Te) phase with very uniform chemical composition. During heat treatment, solid solutions of (Se, Te)ss with different chemical composition were formed with the diffusion of Se atoms into Te solids and Te atoms into Se melts, simultaneously. Then with the increasing temperature, Fe atoms diffused into (Se, Te)ss, Fe(Se, Te)2 and Fe(Se, Te) phases were formed in sequence with the increasing Fe content. The chemical composition in melts became more and more uniform with the further increasing of sintering temperature and dwell time. Therefore, it was suggested that in order to achieve Fe(Se, Te) phase with high superconducting properties, it was necessary to enhance the diffusion process during sintering. The critical temperature of the sample, which was sintered at 700°C for 12h with slow cooling process and an O2-annealing process for 24h, was above 14.0K. This Tc value proved that a good superconducting β phase could be obtained under this sintering condition.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.