Abstract
ABSTRACTThe synthesis of InP/ZnS core/shell nanocrystals and TiO2 nanotubes and the optimization study to couple them together were explored for quantum dot sensitized solar cells. InP/ZnS nanocrystals have advantages of tunable optical properties and intrinsic nontoxicity. Highly luminescent InP/ZnS nanocrystals were produced by precursor-based colloidal synthesis for a photosensitizer. In order to improve on air stability, ZnS shell was grown on InP core. The emission peak was observed at 550 nm. Transmission electron microscopy (TEM) image shows that the nanocrystals highly crystalline and monodisperse. TiO2 nanotube is main inorganic material which is capable of harvesting light as well as being a prominent anode electrode in solar cells. The nanotubular form of TiO2 enhances charge transfer and reduces interfacial charge recombination. Free-standing TiO2 nanotubes were produced by anodization using ammonium fluoride. The free-standing nanotubes were formed under the condition that chemical dissolution speed which depends on fluoride concentration was faster than the speed of Ti oxidation. Electrophoretic deposition was carried out to couple the InP/ZnS nanocrystals with the TiO2 nanotubes. Under an optimized applied voltage condition, the current during the electrophoretic deposition decreased continuously with time. The amount of the deposited nanocrystals was estimated by calculation and the deposited nanocrystals on the TiO2 nanotubes were observed in the TEM.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.