Abstract
This paper describes the effect of frequency and environment on the near-threshold fatigue crack growth behaviour of SA508 cl III reactor pressure vessel (RPV) steel. The study has shown that in the near-threshold regime microstructure and environment markedly affect fatigue crack growth behaviour. In an aqueous environment, fatigue crack growth behaviour became even more sensitive to microstructure, and the fatigue crack growth rate increased by a factor of four in the case of the 3 Hz test, while that for the 0·3 Hz test was increased by a factor of approximately sixteen. This environmental enhancement manifested itself in the form of intergranular failure. For the 0·3 Hz test the percentage intergranular failure decreased from 18% to <1% with an increase in ΔK level. The transition from microstructure-sensitive to microstructure-insensitive occurs when the cyclic plastic zone size is of the order of the prior austenite grain size.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Pressure Vessels and Piping
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.