Abstract
AbstractNowadays, the Gd2Zr2O7 thermal barrier coatings (TBCs) have been evaluated as a promising alternative to yttria‐stabilized zirconia (YSZ). Thus, this investigation focuses on the thermal property, morphology, and failure mechanism of double ceramic layers (DCLs) GdNdZrO/YSZ advanced TBCs. The GdNdZrO coatings with columnar morphology have been deposited on NiCoCrAlYHf bond coating using an electron beam physical vapor deposition method. Material characterizations mainly include X‐ray diffraction, scanning electron microscope, and transmission electron microscopy. The thermal conductivity of GdNdZrO ceramic material is 0.494 W/mK at 1200°C. The thermal shock life of GdNdZrO/YSZ TBCs shows an average shock life of 5235 cycles. The TBC degradation occurs on the crack area within thermally grown oxide layer leading to the interface instability. The interface broken might play an important role in the failure mechanism of TBCs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.