Abstract
The microstructure of silicon nitride hot-pressed with a magnesium oxide additive has been studied by transmission electron microscopy. This includes material at various stages in a hot-pressing process: the initial (∼ 90%α) silicon nitride powder; specimens partially densified and partially transformed from α-silicon “nitride” (Si11.5N15O0.5) to β-silicon nitride (Si3N4); and almost fully dense and fully transformed β-Si3N4. The observations substantiate a solid/liquid/solid transformation mechanism, whereby Si and N are transported from α grains through a silicate liquid phase to nucleation sites for β at α/liquid interfaces or to β grains nucleated homogeneously in the liquid phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.